Part Number | Nominal Size | As supplied(mm) | After recovered (mm) | Standard Length (Meter) | |||
---|---|---|---|---|---|---|---|
(mm) | (Inch) | I.D. | W.T. | I.D(max) | W.T.(min) | ||
G5-YG0016 | 1.6 | 1/16 |
2.0±0.3 |
0.20±0.05 |
0.75 |
0.36 |
200 |
G5-YG0024 | 2.4 | 3/32 |
3.0±0.3 |
0.25±0.05 |
1.25 |
0.44 |
200 |
G5-YG0032 | 3.2 | 1/8 |
3.5±0.3 |
0.25±0.05 |
1.50 |
0.44 |
200 |
G5-YG0048 | 4.8 | 3/16 |
5.0±0.3 |
0.25±0.05 |
2.25 |
0.44 |
100 |
G5-YG0064 | 6.4 | 1/4 |
6.5±0.3 |
0.28±0.05 |
3.0 |
0.56 |
100 |
G5-YG0080 | 8.0 | 5/16 |
8.6±0.3 |
0.30±0.07 |
4.0 |
0.56 |
100 |
G5-YG0095 | 9.5 | 3/8 |
9.6±0.3 |
0.30±0.07 |
4.5 |
0.56 |
100 |
G5-YG0127 | 12.7 | 1/2 |
12.7±0.4 |
0.30±0.07 |
6.0 |
0.56 |
100 |
G5-YG0160 | 16.0 | 5/8 |
16.7±0.5 |
0.35±0.08 |
8.0 |
0.69 |
100 |
G5-YG0191 | 19.1 | 3/4 |
19.0±0.5 |
0.40±0.10 |
9.0 |
0.77 |
100 |
G5-YG0254 | 25.4 | 1 |
26.0±1.0 |
0.45±0.10 |
12.5 |
0.87 |
50 |
G5-YG0318 | 31.8 | 1 1/4 |
31.5±1.0 |
0.45±0.10 |
15.0 |
0.87 |
50 |
G5-YG0381 | 38.1 | 1 1/2 |
41.5±1.0 |
0.50±0.10 |
20.0 |
0.97 |
50 |
G5-YG0508 | 50.8 | 2 |
51.5±1.0 |
0.55±0.10 |
25.0 |
0.97 |
25 |
Property | Specification Requirement | Test Method | Typical Value |
---|---|---|---|
Longitudinal change | -10%~10% | ASTM D2671 | Pass |
Tensile strength | ≥10.3MPa | ASTM D638 | ≥11.3MPa |
Elongation at break | ≥200% | ASTM D638 | ≥400% |
Tensile strength after aging | 70% of initial value | ASTM D638 (158˚C/168 hrs) |
≥80% |
Elongation at break after aging | ≥100% | ASTM D638 (158˚C/168 hrs) |
≥200% |
Heat shock | No cracking | ASTM D2671 (200˚C/4 hrs) |
No cracking |
Low temperature flexibility | No cracking | ASTM D2671 (-55˚C/4 hrs) |
No cracking |
Dielectric voltage withstand | AC2500V/60S no breakdown |
ASTM D2671 | No breakdown |
Volume resistivity | ≥1014Ω.cm | ASTM D876 | ≥1014Ω.cm |
Dielectric strength | ≥19.7KV/mm | ASTM D2671 | 22 KV/mm |
Flammability | VW-1 | UL224 | Pass |