MT2 - Medical-Grade Ultra Thin Wall LDPE Heat Shrinkable Tubing

MT2 - Medical-Grade Ultra Thin Wall LDPE Heat Shrinkable Tubing

Applications:
It is a 2.5:1 shrink ratio medical grade heat shrinkable tubing made of medical grade polyolefin, and satisfies the demand of thin wall and smooth properties which invasive devices required for surgery. The excellent electrical insulation property makes it can be used in the insulation protection of electrosurgical instruments, it’s the heat shrinkable tubing that widely used in medical devices.
Approvals / Specifications:
ISO 10993, RoHS certificated
Operating temperature range
  • Operating temperature: 55˚C~105˚C
  • Minimum shrink temperature: 60˚C
  • Full recovery temperature: Above 110˚C
Color:

black

C

Standard colors: black and clear (Other colors, special sizes, and cut pieces are available on request.)
Inquiry
  • Characteristics
  • Specification
  • Technical Data
  • Shrink ratio: 2.5:1
  • Low shrink temperature
  • High transparency, very flexible
  • Excellent physical, chemical and electrical performance
  • Excellent electrical insulation properties
  • Compatibility with gamma rays and ETO sterilization
  • Double plastic bags and plastic spool package
  • ISO 10993 and RoHS certificates
Part NumberAs supplied (mm)After recovered (mm)
Standard Length (Meter)
I.D.(min)I.D.(max)W.T.

MT2-0010

1.0 0.45 0.25±0.05 200

MT2-0020

2.0 0.80 0.25±0.05 200

MT2-0030

3.0 1.20 0.25±0.05 200

MT2-0060

6.0 2.40 0.25±0.05 100

MT2-0100

10.0 4.00 0.36±0.05 100

 

PropertySpecification RequirementNo crackingTypical Value

Longitudinal change

-10%~10% ASTM D2671 Typical Value

Concentricity

≥70% ASTM D2671 ≥70%

Tensile strength

≥10.3Mpa ASTM D638 ≥10.3Mpa

Volume resistivity

≥1015Ω.cm ASTM D876 ≥1015Ω.cm

Dielectric strength

≥19.7kV/mm ASTM D2671 ≥20kV/mm

Elongation at break

≥120% ASTM D638 ≥140%

Heat shock

No cracking ASTM D2671
(180˚C/4 hrs)
No cracking
Low temperature flexibility No cracking ASTM D2671
(-55˚C/4 hrs)
No cracking

No heavy metals contained

Compatibility with gamma rays and ETO sterilization