AIS - Dual Wall Heat Shrink Tubing, Dual Wall Shrink Tube

Applications:

The outer layer is made of radiation cross-linked polyolefin, and the inner layer is coated with hot melt adhesive. After heating, the outer protective layer is formed, and the inner hot melt adhesive forms an adhesive layer which can protect against water and fix the object firmly, and has good adhesion to rubber, PVC, PE, and aluminum. This tubing can be used in various fields of repairing wires and waterproof requirements.

Approvals / Specifications:
AMS-DTL-23053/4 class3
UL224 File no. E255532, 125℃ VW-1 600V
Operating temperature range:
  • Operating temperature: -45˚C~110˚C
  • Minimum shrink temperature: 80˚C
  • Full recovery temperature: Above 110˚C
Color:

black

Standard color: black (Other colors, special sizes, and cut pieces are available on request.)

Inquiry
  • Characteristics
  • Specification
  • Technical Data
  • Shrink ratio: 3:1 / 4:1
  • Excellent waterproof performance
  • Flexible, high flame retardant
  • Excellent physical, chemical and electrical performance
  • EVA and high melting temperature polyamide (PA) hot melt adhesive are selectable based on your applications
  • Compliance with RoHS and REACH environmental regulations


Part NumberSizeAs supplied (mm)After recovered (mm)Standard Length (Meter)
mmInchI.D.(min)W.T (Nominal Size)I.D.(max)W.T.Adhesive thickness
AIS-3X Shrink ratio
AIS3X0032 3.2 1/8 3.2 0.45 1.0 1.00±0.28 0.45±0.08 200
AIS3X0048 4.8 3/16 4.8 0.45 1.6 1.00±0.28 0.50±0.08 100
AIS3X0064 6.4 1/4 6.4 0.50 2.0 1.00±0.28 0.50±0.08 100
AIS3X0095 9.5 3/8 9.5 0.50 3.0 1.40±0.28 0.60±0.08 50
AIS3X0127 12.7 1/2 12.7 0.65 4.0 1.78±0.38 0.76±0.15 1.22
AIS3X0150 15.0 5/8 15.0 0.60 5.0 1.90±0.38 0.76±0.15 1.22
AIS3X0191 19.1 3/4 19.1 0.70 6.0 2.25±0.55 0.76±0.15 1.22
AIS3X0254 25.4 1 25.4 0.80 8.0 2.54±0.55 1.00±0.20 1.22
AIS3X0381 38.1 1 1/2 38.1 0.80 13.0 2.54±0.55 1.00±0.20 1.22
Part NumberSizeAs supplied (mm)After recovered(mm)Standard Length(Meter)
mmInchI.D.(min)W.T.(Nominal Size)I.D.(max)W.T.Adhesive thickness
AIS-4X Shrink ratio
AIS4X0040 4 3/16 4.0 0.40 1.0 1.00±0.28 0.50±0.08 1.22
AIS4X0080 8 5/16 8.0 0.45 2.0 1.00±0.28 0.50±0.08 1.22
AIS4X0120 12 1/2 12.0 0.45 3.0 1.40±0.28 0.60±0.10 1.22
AIS4X0160 16 5/8 16.0 0.55 4.0 1.78±0.38 0.76±0.15 1.22
AIS4X0240 24 1 24.0 0.70 6.0 2.25±0.55 0.76±0.15 1.22
AIS4X0320 32 1 1/4 32.0 0.70 8.0 2.54±0.55 1.00±0.20 1.22
AIS4X0500 50 2 50.0 0.70 13.0 2.54±0.55 1.00±0.20 1.22
PropertySpecification RequirementTest MethodTypical Value
Longitudinal change -15%~15% ASTM D2671 Pass
Tensile strength ≥10.3MPa ASTM D638 ≥12MPa
Elongation at break ≥200% ASTM D638 ≥400%
Tensile strength after aging 70% of initial value ASTM D638
(158˚C/168 hrs)
≥90%
Elongation at break after aging ≥100% ASTM D638
(158˚C/168 hrs)
≥300%
Heat shock No cracking ASTM D2671
(250˚C/4 hrs)
No cracking
Low temperature flexibility No cracking ASTM D2671
(-30˚C/1 hr)
No cracking
Dielectric voltage withstand AC2500V/60S
No breakdown
ASTM D2671 No breakdown
Volume resistivity ≥1014Ω‧cm ASTM D876 ≥1014Ω‧cm
Copper corrosion No corrosion ASTM D2671
(158˚C/168 hrs)
No corrosion
Flammability VW-1 UL224 Pass