ACS200 - Adhesive Lined Heat Shrinkable Tubing for Wire Harness Assembly


ACS200 is a product with 4:1 high shrink ratio. Inside of the tubing is coated with high performance polyamine hot melt adhesive, which can be fully applied to the waterproof seal of the wire harness multi-wire connection. The 125°C temperature resistant outer layer and 105°C high temperature hot melt adhesive can resist the harsh environment of the automotive industry.

Operating temperature range
  • Continuous operating temperature: -40˚C~125˚C
  • Minimum shrink temperature: 80˚C
  • Full recovery temperature: Above 120˚C


Standard colors: black and clear

  • Characteristics
  • Specification
  • Technical Data
  • Shrink ratio: 4:1
  • Low shrink temperature
  • Flexible, high flame retardant
  • Excellent watertight seal
  • Compliance with RoHS and REACH environmental regulations
Part NumberNominal Size (mm)As supplied (mm)After recovered (mm)Standard Length
I.D.(min)I.D.(max)Adhesive thickness
W.T. (Nominal)
ACS200-1 5.75 5.75 1.25 0.55 1.15 1.22
ACS200-2 7.5 7.5 1.65 0.7 1.40 1.22
ACS200-3 11.0 11.0 2.4 1.0 1.80 1.22
ACS200-4 14.0 14.0 3.0 1.25 2.10 1.22
ACS200-5 18.3 18.3 4.35 1.3 2.10 1.22
PropertySpecification RequirementTest MethodTypical Value
Longitudinal change 0%~10% ASTM D2671 Pass
Tensile strength ≥10MPa ASTM D2671 ≥13MPa
Tensile strength after aging 70% of initial value ASTM D2671
(158˚C/168 hrs)
Elongation at break ≥250% ASTM D2671 ≥300%
Elongation at break after aging ≥200% ASTM D2671
(158˚C/168 hrs)
Heat shock No cracking ASTM D2671
(250˚C/4 hrs)
No cracking
Low temperature flexibility No cracking ASTM D2671
(-40˚C/1 hr)
No cracking
Dielectric voltage withstand AC2500V/60S
No breakdown
ASTM D2671 No breakdown
Volume resistivity ≥1012Ω‧cm ASTM D2671 ≥1012Ω‧cm
Flammability Self extinguishing within 30S after fire source removed. Shrink the tubing onto the axis and torch it vertically for 30 seconds. Pass